Journal Of Raman Spectroscopy
《拉曼光谱学杂志》（Journal of Raman Spectroscopy）
Tian Wang, Senwei Xia, Zhao Ren, Clement Hole, Fen Wang, Jianfeng Zhu, Hongjie Luo, Qiang Li, Meihong Liao, Philippe Sciau
First published: 23 September 2024
首次发表：2024年9月23日
https://doi.org/10.1002/jrs.6736
1 School of Conservation Science & Technology for Cultural Heritage, School of Material Science & Engineering, Key Laboratory of Materials & Technology for Underground Cultural Heritage Conservation, Ministry of Education, Shaanxi University of Science & Technology, 710021 Xi’an, Shaanxi, PR. China
文物保护科学与技术学院、材料科学与工程学院，地下文物保护材料与技术教育部重点实验室，陕西科技大学，中国陕西西安 710021
2 European Synchrotron Radiation Facility, 71 Avenue des Martyrs, 38043 Grenoble, France
欧洲同步辐射装置（ESRF），法国格勒诺布尔烈士大道71号，38043
3 Key Laboratory of Silicate Cultural Relics Conservation (Shanghai University), Ministry of Education, 20444 Shanghai, PR. China
教育部硅酸盐质文物保护重点实验室（上海大学），中国上海 20444
4 Shanghai Institute of Ceramics, Chinese Academy of Sciences, 200050 Shanghai, PR. China
中国科学院上海硅酸盐研究所，中国上海 200050
5 Hongfang Ceramics Co., Ltd., 362500 Dehua, Fujian, PR. China
宏芳陶瓷有限公司，中国福建德化 362500
6 CNRS, CEMES, Toulouse University, 31055 Toulouse, France
法国国家科学研究中心（CNRS）材料结构与结构研究中心（CEMES），图卢兹大学，法国图卢兹 31055
Figure S1 Composition relationship diagram of triangular ingredients for sauce glaze and the firing protocol
图S1 酱釉三角配料组成关系图及烧成制度
Figure S2 The replicate glazed samples (labeled as JY-01-15)
图S2 复制釉样品（标记为JY-01至JY-15）
Figure S3 Optical observation of the glaze surfaces: (a-b) JY-05 and (c-d) JY-14
图S3 釉面光学观察：(a-b) JY-05样品，(c-d) JY-14样品
Figure S4 The reflection spectra of sample JY-05 and JY-14
图S4 JY-05与JY-14样品的反射光谱
Figure S5 Optical observations of crystals in the glaze surfaces
图S5 釉面晶体的光学观察
Funding: This work has been financially supported by the China National Natural Science Foundations (Nos. 62205191, 52272019, and 52272020), Key Scientific Research Project of Shaanxi Provincial Department of Education (No. 22JY008), the Shaanxi Natural Science Basic Research Project (No. 2023WGZJ-YB-45), the Key Laboratory of Silicate Cultural Relics Conservation (Shanghai University), Ministry of Education (No. SCRC2024KF02ZD), and Silicate Cultural Heritage Protection Utilization Innovation Team of Shaanxi Province (No. 2020TD-008). It was performed in the framework of the research collaboration agreement (CNRS No. 186116) between the French National Centre for Scientific Research and the Shaanxi University of Science and Technology.
基金资助：本研究得到中国国家自然科学基金（批准号：62205191、52272019、52272020）、陕西省教育厅重点科研项目（编号：22JY008）、陕西省自然科学基础研究计划项目（编号：2023WGZJ-YB-45）、教育部硅酸盐质文物保护重点实验室（上海大学）开放课题（编号：SCRC2024KF02ZD）以及陕西省硅酸盐文化遗产保护利用创新团队（编号：2020TD-008）的资助。本研究在法国国家科学研究中心（CNRS）与陕西科技大学之间的科研合作协议（CNRS编号：186116）框架下完成。